Ester compounds, polymers, resist compositions and patterning process

ABSTRACT

An ester compound of the following formula (1) is provided.R1 is H, methyl or CH2CO2R3, R2 is H, methyl or CO2R3, R3 is C1-C15 alkyl, k is 0 or 1, Z is a divalent C2-C20 hydrocarbon group which forms a single ring or bridged ring with the carbon atom and which may contain a hetero atom, m is 0 or 1, n is 0, 1, 2 or 3, and 2m+n=2 or 3. A resist composition comprising as the base resin a polymer resulting from the ester compound is sensitive to high-energy radiation, has excellent sensitivity, resolution, and etching resistance, and is suited for micropatterning using electron beams or deep-UV.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to (1) a novel ester compound, (2) a polymer comprising units of the ester compound which is blended as a base resin to formulate a resist composition having a high sensitivity, resolution and etching resistance, and in particular, suitable as micropatterning material for VLSI fabrication, (3) a method for preparing the polymer, (4) a resist composition comprising the polymer, and (5) a patterning process using the resist composition.

2. Prior Art

While a number of recent efforts are being made to achieve a finer pattern rule in the drive for higher integration and operating speeds in LSI devices, deep-ultraviolet lithography is thought to hold particular promise as the next generation in microfabrication technology. In particular, photolithography using a KrF or ArF excimer laser as the light source is strongly desired to reach the practical level as the micropatterning technique capable of achieving a feature size of 0.3 μm or less.

For resist materials for use with a KrF excimer lasers, polyhydroxystyrene having a practical level of transmittance and etching resistance is, in fact, a standard base resin. For resist materials for use with ArF excimer lasers, polyacrylic or polymethacrylic acid derivatives and polymers comprising aliphatic cyclic compounds in the backbone are under investigation. In either case, the basic concept is that some or all of alkali soluble sites of alkali soluble resin are protected with acid labile or eliminatable groups. The overall performance of resist material is adjusted by a choice from among a variety of acid eliminatable protective groups.

Exemplary acid eliminatable protective groups include tert-butoxycarbonyl (JP-B 2-27660), tert-butyl (JP-A 62-115440, JP-A 5-80515, and J. Photopolym. Sci. Technol. 7 [3], 507 (1994)), 2-tetrahydropyranyl (JP-A 2-19847, 5-80515 and 5-88367), and 1-ethoxyethyl (JP-A 2-19847 and 4-215661). While it is desired to achieve a finer pattern rule, none of these acid eliminatable protective groups are deemed to exert satisfactory performance.

More particularly, tert-butoxycarbonyl and tert-butyl are extremely less reactive with acids so that a substantial quantity of energy radiation must be irradiated to generate a sufficient amount of acid in order to establish a difference in rate of dissolution before and after exposure. If a photoacid generator of the strong acid type is used, the exposure can be reduced to a relatively low level because reaction can proceed with a small amount of acid generated. However, in this event, the deactivation of the generated acid by air-borne basic substances has a relatively large influence, giving rise to such problems as a T-top pattern. On the other hand, 2-tetrahydropyranyl and 1-ethoxyethyl are so reactive with acids that with the acid generated by exposure, elimination reaction may randomly proceed without a need for heat treatment, with the result that substantial dimensional changes occur between exposure and heat treatment/development. Where these groups are used as protective groups for carboxylic acid, they have a low dissolution inhibiting effect to alkali, resulting in a high rate of dissolution in unexposed areas and film thinning during development. If highly substituted polymers are used to avoid such inconvenience, there results an extreme drop of heat resistance. These resins fail to provide a difference in rate of dissolution before and after exposure, resulting in resist materials having a very low resolution.

SUMMARY OF THE INVENTION

Therefore, an object of the present invention is to provide (1) a novel ester compound capable of forming an acid-decomposable polymer, (2) a polymer which is blended as a base resin to formulate a resist composition having a higher sensitivity, resolution and etching resistance than conventional resist compositions, (3) a method for preparing the polymer, (4) a resist composition comprising the polymer as a base resin, and (5) a patterning process using the resist composition.

The inventor has found that a novel ester compound of the following general formula (1) obtained by the method to be described later is useful in preparing an acid-decomposable polymer; that a resist composition comprising as the base resin a novel polymer prepared from the ester compound to a weight average molecular weight of 1,000 to 500,000 has a high sensitivity, resolution and etching resistance; and that this resist composition lends itself to precise micropatterning.

In a first aspect, the invention provides an ester compound of the following general formula (1).

Herein R¹ is hydrogen, methyl or CH₂CO₂R³, R² is hydrogen, methyl or CO₂R³, R³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, k is 0 or 1, Z is a divalent hydrocarbon group of 2 to 20 carbon atoms which forms a single ring or bridged ring with the carbon atom and which may contain a hetero atom, m is 0 or 1, n is 0, 1, 2 or 3, and 2m+n is 2 or 3.

In a second aspect, the invention provides a polymer comprising recurring units of the following general formula (1a-1) and/or (1a-2) derived from an ester compound of the general formula (1), and having a weight average molecular weight of 1,000 to 500,000.

Herein R¹, R², Z, k, m and n are as defined above.

In a preferred embodiment, the polymer further comprises recurring units of at least one of the following formulas (2a) to (10a).

Herein R¹, R² and k are as defined above; R⁴ is hydrogen or a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms; at least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms, and the remainders are independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, or R⁵ to R⁸, taken together, may form a ring, and when they form a ring, at least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing divalent hydrocarbon group of 1 to 15 carbon atoms, and the remainders are independently a single bond or a straight, branched or cyclic alkylene group of 1 to 15 carbon atoms; R⁹ is a monovalent hydrocarbon group of 3 to 15 carbon atoms containing a —CO₂— partial structure; at least one of R¹⁰ to R¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing a —CO₂— partial structure, and the remainders are independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, or R¹⁰ to R¹³, taken together, may form a ring, and when they form a ring, at least one of R¹⁰ to R¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing a —CO₂— partial structure, and the remainders are independently a single bond or a straight, branched or cyclic alkylene group of 1 to 15 carbon atoms; R¹⁴ is a polycyclic hydrocarbon group of 7 to carbon atoms or an alkyl group containing such a polycyclic hydrocarbon group; R¹⁵ is an acid labile group; X is —CH₂— or —O—; and Y is —O— or —(NR¹⁶)— wherein R¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms.

In a third aspect, the invention provides a method for preparing a polymer comprising the step of effecting radical polymerization, anionic polymerization or coordination polymerization between an ester compound of the general formula (1) and another compound having a carbon-to-carbon double bond.

In a fourth aspect, the invention provides a resist composition comprising the polymer defined above, and more specifically, a resist composition comprising the polymer defined above, a photoacid generator, and an organic solvent.

In a fifth aspect, the invention provides a process for forming a resist pattern comprising the steps of applying the resist composition defined above onto a substrate to form a coating; heat treating the coating and then exposing it to high-energy radiation or electron beams through a photo mask; and optionally heat treating the exposed coating and developing it with a developer.

The ester compound of formula (1) and the polymer comprising units of formula (1a-1) and/or (1a-2) employ a cycloalkylcycloalkyl or cycloalkylcycloalkenyl group of the following formula (1b) as the acid-eliminatable protective group, thereby overcoming the drawbacks of the tert-butoxycarbonyl and tert-butyl groups having low reactivity with acid as well as the 2-tetrahydropyranyl and 1-ethoxyethyl groups having too high reactivity with acid and low resistance to alkaline developers.

Herein, Z, m and n are as defined above, the broken line denotes a valence bond.

The ester compound of formula (1) is decomposed under acidic conditions while generating an olefin compound and a carboxylic acid. This mechanism itself is apparently identical with the decomposition of tertiary alkyl esters such as tert-butyl esters although the decomposition rate significantly differs between them. In the acidolysis of a tertiary alkyl ester, carboxylic acid and a tertiary alkyl cation generate first, then the extinction of the cation due to proton release occurs to form an olefin compound, whereby the reaction comes to an end. The rate-determining stage of this decomposition reaction is the late stage of cation extinction. The progress of this stage is very rapid in the case of the ester compound of formula (1), probably because the moderated distortion of the ring and the formation of a conjugated system produce a strong thrust. The olefin compound produced has a very low re-reactivity. As a consequence, the ester compound of formula (1) provides a high degree of acidolysis surpassing other tertiary alkyl esters.

Since the ester compound of formula (1) is basically a tertiary alkyl ester, it, when formulated into a resist composition, does not allow for the infinite progress of decomposition in a duration between exposure and development and film thinning during development as found with 2-tetrahydropyranyl and 1-ethoxyethyl. When a polymer comprising constituent units derived from the compound is formulated as the base resin, there is obtained a resist composition which possesses a high sensitivity and resolution and has a high dissolution contrast in that the unexposed areas have a very slow rate of dissolution while the areas having undergone an adequate dose of exposure quickly become alkali soluble. Additionally, very high etching resistance is exerted by virtue of the robust aliphatic ring positioned on the backbone of the polymer and a plurality of aliphatic rings contained in the protective group of formula (1b).

BRIEF DESCRIPTION OF THE DRAWING

The only FIGURE, FIG. 1 is a diagram showing the ¹H-NMR spectrum of the monomer obtained in Synthesis Example 1.

DESCRIPTION OF THE PREFERRED EMBODIMENT

Ester Compound

The novel ester compounds according to the first aspect of the invention are of the following general formula (1).

Herein, R¹ is hydrogen, methyl or CH₂CO₂R³. R² is hydrogen, methyl or CO₂R³. R³ stands for straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms, such as, for example, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl and butyladamantyl.

Z is a divalent hydrocarbon group of 2 to 20 carbon atoms which forms a single ring or bridged ring with the carbon atom and which may contain a hetero atom, for example, single ring-forming hydrocarbon groups such as cyclopropane, cyclobutane, cyclopentane, cyclohexane, cycloheptane, and cyclooctane; bridged ring-forming hydrocarbon groups such as bicyclo[2.2.1]heptane, bicyclo[2.2.2]octane, bicyclo[4.4.0]decane and tricyclo[5.2.1.0^(2,6)]decane; and ring-forming hydrocarbon groups in which some of the hydrogen atoms in the foregoing groups are substituted with alkyl, hydroxy, alkoxy, acyloxy, alkylcarbonyl, hydroxycarbonyl, alkoxycarbonyl and oxo, among others.

The letter k is 0 or 1, m is 0 or 1, n is 0, 1, 2 or 3, and 2m+n is equal to 2 or 3.

Illustrative, non-limiting, examples of the ester compounds of the invention are given below.

The ester compound of the invention is prepared, for example, by the following process, although the preparation is not limited thereto.

Herein, R¹, R², Z, k, m and n are as defined above, and Hal is bromine or chlorine.

Step A is to effect nucleophilic addition reaction with the carbonyl on a cyclic ketone compound to form a tertiary alcohol. This stage is typified by Grignard reaction, but not limited thereto. Reaction readily takes place under well-known conditions, preferably by mixing the reactants: cyclic ketone compound, alkyl halide and magnesium in a solvent such as tetrahydrofuran or diethyl ether, while heating or cooling the reaction mixture if desired.

Step B is to convert the tertiary alcohol to an ester of unsaturated acid. Reaction readily takes place under well-known conditions, preferably by mixing the reactants: tertiary alcohol, unsaturated carboxylic halide (e.g., acrylic chloride or methacrylic chloride) and base (e.g., triethylamine) in a solvent such as methylene chloride, while cooling the reaction mixture if desired.

Step C is to construct an alicyclic skeleton through Diels-Alder reaction. Reaction readily takes place under well-known conditions, preferably by mixing the reactants: ester of unsaturated acid and cyclopentadiene in a solventless system or in a solvent such as benzene, optionally in the presence of a catalyst such as boron trifluoride, while heating or cooling the reaction mixture if desired.

Polymer

In the second aspect, the invention provides a polymer or high molecular weight compound comprising recurring units of the following general formula (1a-1) and/or (1a-2) derived from an ester compound of the general formula (1), and having a weight average molecular weight of 1,000 to 500,000, and preferably 5,000 to 100,000.

Herein R¹, R², Z, k, m and n are as defined above.

The polymer of the invention may further comprise recurring units of at least one type selected from recurring units of the following formulas (2a) to (10a) which are derived from monomers of the following general formulas (2) to (10).

In the above formulae, X is —CH₂— or —O—; Y is —O— or —(NR¹⁶)— wherein R¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms; and k is equal to 0 or 1. Then formulae (6a-1) to (9a-2) may also be represented by the following formulae (6a-1-1) to (9a-2-2).

Herein R¹ and R² are as defined above.

R⁴ stands for hydrogen or carboxyl or hydroxyl-containing monovalent hydrocarbon groups of 1 to 15 carbon atoms, for example, carboxyethyl, carboxybutyl, carboxycyclopentyl, carboxycyclohexyl, carboxynorbornyl, carboxyadamantyl, hydroxyethyl, hydroxybutyl, hydroxycyclopentyl, hydroxycyclohexyl, hydroxynorbornyl, and hydroxyadamantyl.

At least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms, and the remaining R's are independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Examples of the carboxyl or hydroxyl-bearing monovalent hydrocarbon group of 1 to 15 carbon atoms include carboxy, carboxymethyl, carboxyethyl, carboxybutyl, hydroxymethyl, hydroxyethyl, hydroxybutyl, 2-carboxy-ethoxycarbonyl, 4-carboxybutoxycarbonyl, 2-hydroxyethoxycarbonyl, 4-hydroxybutoxycarbonyl, carboxycyclopentyloxycarbonyl, carboxycyclohexyloxycarbonyl, carboxynorbornyloxycaronyl, carboxyadamantyloxycarbonyl, hydroxycyclopentyloxycarbonyl, hydroxycyclohexyloxycarbonyl, hydroxynorbornyloxycarbonyl, and hydroxyadamantyloxycarbonyl. Examples of the straight, branched or cyclic alkyl group of 1 to 15 carbon atoms are the same as exemplified for R³ . R⁵ to R⁸, taken together, may form a ring, and in that event, at least one of R⁵ to R⁸ is a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. Examples of the carboxyl or hydroxyl-bearing divalent hydrocarbon group of 1 to 15 carbon atoms include the groups exemplified as the carboxyl or hydroxyl-bearing monovalent hydrocarbon group, with one hydrogen atom eliminated therefrom. Examples of the straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms include the groups exemplified for R³, with one hydrogen atom eliminated therefrom.

R⁹ is a monovalent hydrocarbon group of 3 to 15 carbon atoms containing a —CO₂— partial structure, for example, 2-oxooxolan-3-yl, 4,4-dimethyl-2-oxooxolan-3-yl, 4-methyl-2-oxooxan-4-yl, 2-oxo-1,3-dioxolan-4-ylmethyl, and 5-methyl-2-oxooxolan-5-yl. At least one of R¹⁰ to R¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing a —CO₂— partial structure, while the remaining R's are independently hydrogen or straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms. Examples of the monovalent hydrocarbon group of 2 to 15 carbon atoms containing a —CO₂— partial structure include 2-oxooxolan-3-yloxycarbonyl, 4,4-dimethyl-2-oxooxolan-3-yloxycarbonyl, 4-methyl-2-oxooxan-4-yloxycarbonyl, 2-oxo-1,3-dioxolan-4-ylmethyloxycarbonyl, and 5-methyl-2-oxooxolan-5-yloxycarbonyl. Examples of the straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms are the same as exemplified for R³. R¹⁰ to R¹³, taken together, may form a ring, and in that event, at least one of R¹⁰ to R¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing a —CO₂— partial structure, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. Examples of the divalent hydrocarbon group of 1 to 15 carbon atoms containing a —CO₂— partial structure include 1-oxo-2-oxapropane-1,3-diyl, 1,3-dioxo-2-oxapropane-1,3-diyl, 1-oxo-2-oxabutane-1,4-diyl, and 1,3-dioxo-2-oxabutane-1,4-diyl, as well as the groups exemplified as the monovalent hydrocarbon group containing a —CO₂— partial structure, with one hydrogen atom eliminated therefrom. Examples of the straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms include the groups exemplified for R³ ₁ with one hydrogen atom eliminated therefrom.

R¹⁴ is a polycyclic hydrocarbon group having 7 to 15 carbon atoms or an alkyl group containing a polycyclic hydrocarbon group, for example, norbornyl, bicyclo[3.3.1]-nonyl, tricyclo[5.2.1.0.^(2,6)]decyl, adamantyl, ethyladamantyl, butyladamantyl, norbornylmethyl, and adamantylmethyl.

R¹⁵ is an acid labile group, and k is 0 or 1.

X is —CH₂— or —O—.

Y is —O— or —(NR¹⁶)— wherein R¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, examples of which are as described for R³.

The acid labile groups represented by R¹⁵ may be selected from a variety of such groups. Examples of the acid labile group are groups of the following general formulae (L1) to (L4), tertiary alkyl groups of 4 to 20 carbon atoms, preferably 4 to 15 carbon atoms, trialkylsilyl groups in which each alkyl moiety has 1 to 6 carbon atoms, and oxoalkyl groups of 4 to 20 carbon atoms.

R^(L01) and R^(L02) are hydrogen or straight, branched or cyclic alkyl groups of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms. Exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, cyclopentyl, cyclohexyl, 2-ethylhexyl, and n-octyl. R^(L03) is a monovalent hydrocarbon group of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms, which may contain a hetero atom such as oxygen, examples of which include unsubstituted straight, branched or cyclic alkyl groups and straight, branched or cyclic alkyl groups in which some hydrogen atoms are replaced by hydroxyl, alkoxy, oxo, amino, alkylamino or the like. Illustrative examples are the substituted alkyl groups shown below.

A pair of R^(L01) and R^(L02), R^(L01) and R^(L03), or R^(L02) and R^(L03) may form a ring. Each of R^(L01), R^(L02) and R^(L03) is a straight or branched alkylene group of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms when they form a ring.

R^(L04) is a tertiary alkyl group of 4 to 20 carbon atoms, preferably 4 to 15 carbon atoms, a trialkylsilyl group in which each alkyl moiety has 1 to 6 carbon atoms, an oxoalkyl group of 4 to 20 carbon atoms, or a group of formula (L1). Exemplary tertiary alkyl groups are tert-butyl, tert-amyl, 1,1-diethylpropyl, 1-ethylcyclopentyl, 1-butylcyclopentyl, 1-ethylcyclohexyl, 1-butylcyclohexyl, 1-ethyl-2-cyclopentenyl, 1-ethyl-2-cyclohexenyl, and 2-methyl-2-adamantyl. Exemplary trialkylsilyl groups are trimethylsilyl, triethylsilyl, and dimethyl-tert-butylsilyl. Exemplary oxoalkyl groups are 3-oxocyclohexyl, 4-methyl-2-oxooxan-4-yl, and 5-methyl-5-oxooxolan-4-yl. Letter y is an integer of 0 to 6.

R^(L05) is a straight or branched alkyl group of 1 to 8 carbon atoms or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. Examples of the straight, branched or cyclic alkyl group include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl and n-hexyl. Exemplary aryl groups are phenyl, methylphenyl, naphthyl, anthryl, phenanthryl, and pyrenyl. Letter m is equal to 0 or 1, n is equal to 0, 1, 2 or 3, and 2m+n is equal to 2 or 3.

R^(L06) is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. Examples of these groups are the same as exemplified for R^(L05).

R^(L07) to R^(L16) independently represent hydrogen or monovalent hydrocarbon groups of 1 to 15 carbon atoms which may contain a hetero atom. Exemplary hydrocarbon groups are straight, branched or cyclic alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, n-octyl, n-nonyl, n-decyl, cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl and cyclohexylbutyl, and substituted ones of these groups in which some hydrogen atoms are replaced by hydroxyl, alkoxy, carboxy, alkoxycarbonyl, oxo, amino, alkylamino, cyano, mercapto, alkylthio, sulfo or other groups. Alternatively, R^(L07) to R^(L16), taken together, form a ring (for example, a pair of R^(L07) and R^(L08), R^(L07) and R^(L09), R^(L08) and R^(L10), R^(L09) and R^(L10), R^(L11) and R^(L12), R^(L13) and R^(L14), or a similar pair form a ring). Each of R^(L07) to R^(L16) represents a divalent C₁-C₁₅ hydrocarbon group which may contain a hetero atom, when they form a ring, examples of which are the ones exemplified above for the monovalent hydrocarbon groups, with one hydrogen atom being eliminated. Two of R^(L07) to R^(L16) which are attached to adjoining carbon atoms (for example, a pair of R^(L07) and R^(L09), R^(L09) and R^(L15), R^(L13) and R^(L15), or a similar pair) may bond together directly to form a double bond.

Of the acid labile groups of formula (L1), the straight and branched ones are exemplified by the following groups.

Of the acid labile groups of formula (L1), the cyclic ones are, for example, tetrahydrofuran-2-yl, 2-methyltetrahydrofuran-2-yl, tetrahydropyran-2-yl, and 2-methyltetrahydropyran-2-yl.

Examples of the acid labile groups of formula (L2) include tert-butoxycarbonyl, tert-butoxycarbonylmethyl, tert-amyloxycarbonyl, tert-amyloxycarbonylmethyl, 1,1-diethylpropyloxycarbonyl, 1,1-diethylpropyloxycarbonylmethyl, 1-ethylcyclopentyloxycarbonyl, 1-ethylcyclopentyloxycarbonylmethyl, 1-ethyl-2-cyclopentenyloxycarbonyl, 1-ethyl-2-cyclopentenyloxycarbonylmethyl, 1-ethoxyethoxycarbonylmethyl, 2-tetrahydropyranyloxycarbonylmethyl, and 2-tetrahydrofuranyloxycarbonylmethyl groups.

Examples of the acid labile groups of formula (L3) include 1-methylcyclopentyl, 1-ethylcyclopentyl, 1-n-propylcyclopentyl, 1-isopropylcyclopentyl, 1-n-butylcyclopentyl, 1-sec-butylcyclopentyl, 1-methylcyclohexyl, 1-ethylcyclohexyl, 3-methyl-1-cyclopenten-3-yl, 3-ethyl-1-cyclopenten-3-yl, 3-methyl-1-cyclohexen-3-yl, and 3-ethyl-1-cyclohexen-3-yl groups.

The acid labile groups of formula (L4) are exemplified by the following groups.

The polymer of the invention may be prepared by polymerizing an ester compound of formula (1) or by copolymerizing a first monomer in the form of an ester compound of formula (1) with a second monomer in the form of at least one compound of formulas (2) to (10). By properly adjusting the proportion of the respective monomers used in a the copolymerization reaction, the polymer can be tailored so that it may exert the preferred performance when blended in resist compositions.

In addition to (i) the monomer of formula (1) and (ii) the monomer or monomers of formulas (2) to (10), the polymer of the invention may have copolymerized therewith (iii) another monomer having a carbon-to-carbon double bond other than (i) and (ii). Examples of the additional monomer (iii) include substituted acrylic acid esters such as methyl methacrylate, methyl crotonate, dimethyl maleate, and dimethyl itaconate, unsaturated carboxylic acids such as maleic acid, fumaric acid and itaconic acid, substituted or unsubstituted norbornenes such as norbornene and methyl norbornene-5-carboxylate, and unsaturated acid anhydrides such as itaconic anhydride.

The polymers of the invention may contain

(I) more than 0 mol % to 100 mol %, preferably 20 to 90 mol %, more preferably 30 to 80 mol % of units of formula (1a-1) and/or (1a-2) derived from the monomer of formula (1),

(II) 0 mol % to less than 100 mol %, preferably 1 to 95 mol %, more preferably 5 to 90 mol % of units of one or more types of formulae (2a) to (10a) derived from the monomers of formulae (2) to (10), and optionally,

(III) 0 to 80 mol %, preferably 0 to 70 mol %, more preferably 0 to 50 mol % of units of one or more types derived from the additional monomers (iii).

The polymers of the invention have a weight average molecular weight of 1,000 to 500,000, preferably 3,000 to 100,000. Outside the range, the etching resistance may become extremely low and the resolution may become low because a substantial difference in rate of dissolution before and after exposure is lost.

In the method according to the third aspect of the invention, a polymer is prepared by effecting radical polymerization, anionic polymerization or coordination polymerization between an ester compound of formula (1) and another compound having a carbon-to-carbon double bond, which is typically selected from the above-described monomers (ii) and (iii).

For radical polymerization, preferred reaction conditions include (a) a solvent selected from among hydrocarbons such as benzene, ethers such as tetrahydrofuran, alcohols such as ethanol, and ketones such as methyl isobutyl ketone, (b) a polymerization initiator selected from azo compounds such as 2,2′-azobisisobutyronitrile and peroxides such as benzoyl peroxide and lauroyl peroxide, (c) a temperature of about 0° C. to about 100° C., and (d) a time of about ½ hour to about 48 hours. Reaction conditions outside the described range may be employed if desired.

For anionic polymerization, preferred reaction conditions include (a) a solvent selected from among hydrocarbons such as benzene, ethers such as tetrahydrofuran, and liquid ammonia, (b) a polymerization initiator selected from metals such as sodium and potassium, alkyl metals such as n-butyllithium and sec-butyllithium, ketyl, and Grignard reagents, (c) a temperature of about −78° C. to about 0° C., (d) a time of about ½ hour to about 48 hours, and (e) a stopper selected from among proton-donative compounds such as methanol, halides such as methyl iodide, and electrophilic compounds. Reaction conditions outside the described range may be employed if desired.

For coordination polymerization, preferred reaction conditions include (a) a solvent selected from among hydrocarbons such as n-heptane and toluene, (b) a catalyst selected from Ziegler-Natta catalysts comprising a transition metal (e.g., titanium) and alkylaluminum, Phillips catalysts of metal oxides having chromium or nickel compounds carried thereon, and olefin-metathesis mixed catalysts as typified by tungsten and rhenium mixed catalysts, (c) a temperature of about 0° C. to about 100° C., and (d) a time of about ½ hour to about 48 hours. Reaction conditions outside the described range may be employed if desired.

Resist Composition

Since the polymer of the invention is useful as the base polymer of a resist composition, the other aspect of the invention provides a resist composition comprising the polymer. Specifically, the resist composition is defined as comprising the polymer, a photoacid generator, and an organic solvent.

Photoacid Generator

The photoacid generator is a compound capable of generating an acid upon exposure to high energy radiation or electron beams and includes the following:

(i) onium salts of the formula (P1a-1), (P1a-2) or (P1b),

(ii) diazomethane derivatives of the formula (P2),

(iii) glyoxime derivatives of the formula (P3),

(iv) bissulfone derivatives of the formula (P4),

(v) sulfonic acid esters of N-hydroxyimide compounds of the formula (P5),

(vi) β-ketosulfonic acid derivatives,

(vii) disulfone derivatives,

(viii) nitrobenzylsulfonate derivatives, and

(ix) sulfonate derivatives.

These photoacid generators are described in detail.

(i) Onium salts of formula (P1a-1), (P1a-2) or (P1b):

Herein, R^(101a), R^(101b), and R^(101c) independently represent straight, branched or cyclic alkyl, alkenyl, oxoalkyl or oxoalkenyl groups of 1 to 12 carbon atoms, aryl groups of 6 to 20 carbon atoms, or aralkyl or aryloxoalkyl groups of 7 to 12 carbon atoms, wherein some or all of the hydrogen atoms may be replaced by alkoxy or other groups. Also, R^(101b) and R^(101c), taken together, may form a ring. R^(101b) and R^(101c) each are alkylene groups of 1 to 6 carbon atoms when they form a ring. K⁻ is a non-nucleophilic counter ion.

R^(101a), R^(101b), and R^(101c) may be the same or different and are illustrated below. Exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclopropylmethyl, 4-methylcyclohexyl, cyclohexylmethyl, norbornyl, and adamantyl. Exemplary alkenyl groups include vinyl, allyl, propenyl, butenyl, hexenyl, and cyclohexenyl. Exemplary oxoalkyl groups include 2-oxocyclopentyl and 2-oxocyclohexyl as well as 2-oxopropyl, 2-cyclopentyl-2-oxoethyl, 2-cyclohexyl-2-oxoethyl, and 2-(4-methylcyclohexyl)-2-oxoethyl. Exemplary aryl groups include phenyl and naphthyl; alkoxyphenyl groups such as p-methoxyphenyl, m-methoxyphenyl, o-methoxyphenyl, ethoxyphenyl, p-tert-butoxyphenyl, and m-tert-butoxyphenyl; alkylphenyl groups such as 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, ethylphenyl, 4-tert-butylphenyl, 4-butylphenyl, and dimethylphenyl; alkylnaphthyl groups such as methylnaphthyl and ethylnaphthyl; alkoxynaphthyl groups such as methoxynaphthyl and ethoxynaphthyl; dialkylnaphthyl groups such as dimethylnaphthyl and diethylnaphthyl; and dialkoxynaphthyl groups such as dimethoxynaphthyl and diethoxynaphthyl. Exemplary aralkyl groups include benzyl, phenylethyl, and phenethyl. Exemplary aryloxoalkyl groups are 2-aryl-2-oxoethyl groups such as 2-phenyl-2-oxoethyl, 2-(1-naphthyl)-2-oxoethyl, and 2-(2-naphthyl)-2-oxoethyl. Examples of the non-nucleophilic counter ion represented by K⁻ include halide ions such as chloride and bromide ions, fluoroalkylsulfonate ions such as triflate, 1,1,1-trifluoroethanesulfonate, and nonafluorobutanesulfonate, arylsulfonate ions such as tosylate, benzenesulfonate, 4-fluorobenzenesulfonate, and 1,2,3,4,5-pentafluorobenzenesulfonate, and alkylsulfonate ions such as mesylate and butanesulfonate.

Herein, R^(102a) and R^(102b) independently represent straight, branched or cyclic alkyl groups of 1 to 8 carbon atoms. R¹⁰³ represents a straight, branched or cyclic alkylene groups of 1 to 10 carbon atoms. R^(104a) and R^(104b) independently represent 2-oxoalkyl groups of 3 to 7 carbon atoms. K⁻ is a non-nucleophilic counter ion.

Illustrative of the groups represented by R^(102a) and R^(102b) are methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, cyclopentyl, cyclohexyl, cyclopropylmethyl, 4-methylcyclohexyl, and cyclohexylmethyl. Illustrative of the groups represented by R^(L03) are methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, 1,4-cyclohexylene, 1,2-cyclohexylene, 1,3-cyclopentylene, 1,4-cyclooctylene, and 1,4-cyclohexanedimethylene. Illustrative of the groups represented by R^(104a) and R^(104b) are 2-oxopropyl, 2-oxocyclopentyl, 2-oxocyclohexyl, and 2-oxocycloheptyl. Illustrative examples of the counter ion represented by K⁻ are the same as exemplified for formulae (P1a-1) and (P1a-2).

(ii) Diazomethane derivatives of formula (P2)

Herein, R¹⁰⁵ and R¹⁰⁶ independently represent straight, branched or cyclic alkyl or halogenated alkyl groups of 1 to 12 carbon atoms, aryl or halogenated aryl groups of 6 to 20 carbon atoms, or aralkyl groups of 7 to 12 carbon atoms.

Of the groups represented by R¹⁰⁵ and R¹⁰⁶, exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, amyl, cyclopentyl, cyclohexyl, cycloheptyl, norbornyl, and adamantyl. Exemplary halogenated alkyl groups include trifluoromethyl, 1,1,1-trifluoroethyl, 1,1,1-trichloroethyl, and nonafluorobutyl. Exemplary aryl groups include phenyl; alkoxyphenyl groups such as p-methoxyphenyl, m-methoxyphenyl, o-methoxyphenyl, ethoxyphenyl, p-tert-butoxyphenyl, and m-tert-butoxyphenyl; and alkylphenyl groups such as 2-methyl-phenyl, 3-methylphenyl, 4-methylphenyl, ethylphenyl, 4-tert-butylphenyl, 4-butylphenyl, and dimethylphenyl. Exemplary halogenated aryl groups include fluorophenyl, chlorophenyl, and 1,2,3,4,5-pentafluorophenyl. Exemplary aralkyl groups include benzyl and phenethyl.

(iii) Glyoxime derivatives of formula (P3)

Herein, R¹⁰⁷, R¹⁰⁸, and R¹⁰⁹ independently represent straight, branched or cyclic alkyl or halogenated alkyl groups of 1 to 12 carbon atoms, aryl or halogenated aryl groups of 6 to 20 carbon atoms, or aralkyl groups of 7 to 12 carbon atoms. Also, R¹⁰⁸ and R¹⁰⁹, taken together, may form a ring. R¹⁰⁸ and R¹⁰⁹ each are straight or branched alkylene groups of 1 to 6 carbon atoms when they form a ring.

Illustrative examples of the alkyl, halogenated alkyl, aryl, halogenated aryl, and aralkyl groups represented by R¹⁰⁷, R¹⁰⁸, and R¹⁰⁹ are the same as exemplified for R¹⁰⁵ and R¹⁰⁶. Examples of the alkylene groups represented by R¹⁰⁸ and R¹⁰⁹ include methylene, ethylene, propylene, butylene, and hexylene.

(iv) Bissulfone derivatives of formula (P4)

Herein, R^(101a) and R^(101b) are as defined above.

(v) Sulfonic acid esters of N-hydroxyimide compounds of formula (P5)

Herein, R¹¹⁰ is an arylene group of 6 to 10 carbon atoms, alkylene group of 1 to 6 carbon atoms, or alkenylene group of 2 to 6 carbon atoms wherein some or all of the hydrogen atoms may be replaced by straight or branched alkyl or alkoxy groups of 1 to 4 carbon atoms, nitro, acetyl, or phenyl groups. R¹¹¹ is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms, alkenyl, alkoxyalkyl, phenyl or naphthyl group wherein some or all of the hydrogen atoms may be replaced by alkyl or alkoxy groups of 1 to 4 carbon atoms, phenyl groups (which may have substituted thereon an alkyl or alkoxy of 1 to 4 carbon atoms, nitro, or acetyl group), hetero-aromatic groups of 3 to 5 carbon atoms, or chlorine or fluorine atoms.

Of the groups represented by R¹¹⁰, exemplary arylene groups include 1,2-phenylene and 1,8-naphthylene; exemplary alkylene groups include methylene, 1,2-ethylene, 1,3-propylene, 1,4-butylene, 1-phenyl-1,2-ethylene, and norbornane-2,3-diyl; and exemplary alkenylene groups include 1,2-vinylene, 1-phenyl-1,2-vinylene, and 5-norbornene-2,3-diyl. Of the groups represented by R¹¹¹, exemplary alkyl groups are as exemplified for R^(101a) to R^(101c); exemplary alkenyl groups include vinyl, 1-propenyl, allyl, 1-butenyl, 3-butenyl, isoprenyl, 1-pentenyl, 3-pentenyl, 4-pentenyl, dimethylallyl, 1-hexenyl, 3-hexenyl, 5-hexenyl, 1-heptenyl, 3-heptenyl, 6-heptenyl, and 7-octenyl; and exemplary alkoxyalkyl groups include methoxymethyl, ethoxymethyl, propoxymethyl, butoxymethyl, pentyloxymethyl, hexyloxymethyl, heptyloxymethyl, methoxyethyl, ethoxyethyl, propoxyethyl, butoxyethyl, pentyloxyethyl, hexyloxyethyl, methoxypropyl, ethoxypropyl, propoxypropyl, butoxypropyl, methoxybutyl, ethoxybutyl, propoxybutyl, methoxypentyl, ethoxypentyl, methoxyhexyl, and methoxyheptyl.

Of the substituents on these groups, the alkyl groups of 1 to 4 carbon atoms include methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl and tert-butyl; the alkoxy groups of 1 to 4 carbon atoms include methoxy, ethoxy, propoxy, isopropoxy, n-butoxy, isobutoxy, and tert-butoxy; the phenyl groups which may have substituted thereon an alkyl or alkoxy of 1 to 4 carbon atoms, nitro, or acetyl group include phenyl, tolyl, p-tert-butoxyphenyl, p-acetylphenyl and p-nitrophenyl; the hetero-aromatic groups of 3 to 5 carbon atoms include pyridyl and furyl.

Illustrative examples of the photoacid generator include:

onium salts such as diphenyliodonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)phenyliodonium trifluoromethanesulfonate, diphenyliodonium p-toluene-sulfonate, (p-tert-butoxyphenyl)phenyliodonium p-toluene-sulfonate, triphenylsulfonium trifluoromethanesulfonate, (p-tert-butoxyphenyl) diphenylsulfonium trifluoromethanesulfonate, bis(p-tert-butoxyphenyl)phenylsulfonium trifluoromethanesulfonate, tris(p-tert-butoxyphenyl)sulfonium trifluoromethanesulfonate, triphenylsulfonium p-toluenesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium p-toluenesulfonate, bis(p-tert-butoxyphenyl)phenylsulfonium p-toluenesulfonate, tris(p-tert-butoxyphenyl)sulfonium p-toluenesulfonate, triphenylsulfonium nonafluorobutane-sulfonate, triphenylsulfonium butanesulfonate, trimethylsulfonium trifluoromethanesulfonate, trimethylsulfonium p-toluenesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl) sulfonium p-toluenesulfonate, dimethylphenylsulfonium trifluoromethanesulfonate, dimethylphenylsulfonium p-toluenesulfonate, dicyclohexylphenylsulfonium trifluoromethanesulfonate, dicyclohexylphenylsulfonium p-toluenesulfonate, trinaphthylsulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, (2-norbornyl)methyl(2-oxocyclohexyl) sulfonium trifluoromethanesulfonate, ethylenebis-[methyl(2-oxocyclopentyl)sulfonium trifluoromethanesulfonate], and 1,2′-naphthylcarbonylmethyltetrahydrothiophenium triflate;

diazomethane derivatives such as bis(benzenesulfonyl)diazomethane, bis(p-toluenesulfonyl)diazomethane, bis(xylenesulfonyl)diazomethane, bis(cyclohexylsulfonyl)diazomethane, bis(cyclopentylsulfonyl)diazomethane, bis(n-butylsulfonyl)diazomethane, bis(isobutylsulfonyl)diazomethane, bis(sec-butylsulfonyl)diazomethane, bis(n-propylsulfonyl)diazomethane, bis(isopropylsulfonyl)diazomethane, bis(tert-butylsulfonyl)diazomethane, bis(n-amylsulfonyl)diazomethane, bis(isoamylsulfonyl)diazomethane, bis(sec-amylsulfonyl)diazomethane, bis(tert-amylsulfonyl)diazomethane, 1-cyclohexylsulfonyl-1-(tert-butylsulfonyl)diazomethane, 1-cyclohexylsulfonyl-1-(tert-amylsulfonyl)diazomethane, and 1-tert-amylsulfonyl-1-(tert-butylsulfonyl)diazomethane;

glyoxime derivatives such as bis-o-(p-toluenesulfonyl)-α-dimethylglyoxime, bis-o-(p-toluenesulfonyl)-α-diphenylglyoxime, bis-o-(p-toluenesulfonyl)-α-dicyclohexylglyoxime, bis-o-(p-toluenesulfonyl)-2,3-pentanedioneglyoxime, bis-o-(p-toluenesulfonyl)-2-methyl-3,4-pentanedioneglyoxime, bis-o-(n-butanesulfonyl)-α-dimethylglyoxime, bis-o-(n-butanesulfonyl)-α-diphenylglyoxime, bis-o-(n-butanesulfonyl)-α-dicyclohexylglyoxime, bis-o-(n-butanesulfonyl)-2,3-pentanedioneglyoxime, bis-o-(n-butanesulfonyl)-2-methyl-3,4-pentanedioneglyoxime, bis-o-(methanesulfonyl)-α-dimethylglyoxime, bis-o-(trifluoromethanesulfonyl)-α-dimethylglyoxime, bis-o-(1,1,1-trifluoroethanesulfonyl)-α-dimethylglyoxime, bis-o-(tert-butanesulfonyl)-α-dimethylglyoxime, bis-o-(perfluorooctanesulfonyl)-α-dimethylglyoxime, bis-o-(cyclohexanesulfonyl)-α-dimethylglyoxime, bis-o-(benzenesulfonyl)-α-dimethylglyoxime, bis-o-(p-fluorobenzenesulfonyl)-α-dimethylglyoxime, bis-o-(p-tert-butylbenzenesulfonyl)-α-dimethylglyoxime, bis-o-(xylenesulfonyl)-α-dimethylglyoxime, and bis-o-(camphorsulfonyl)-α-dimethylglyoxime;

bissulfone derivatives such as bisnaphthylsulfonylmethane, bistrifluoromethylsulfonylmethane, bismethylsulfonylmethane, bisethylsulfonylmethane, bispropylsulfonylmethane, bisisopropylsulfonylmethane, bis-p-toluenesulfonylmethane, and bisbenzenesulfonylmethane;

β-ketosulfone derivatives such as 2-cyclohexylcarbonyl-2-(p-toluenesulfonyl)propane and 2-isopropylcarbonyl-2-(p-toluenesulfonyl)propane;

disulfone derivatives such as diphenyl disulfone and dicyclohexyl disulfone;

nitrobenzyl sulfonate derivatives such as 2,6-dinitrobenzyl p-toluenesulfonate and 2,4-dinitrobenzyl p-toluenesulfonate;

sulfonic acid ester derivatives such as 1,2,3-tris-(methanesulfonyloxy)benzene, 1,2,3-tris(trifluoromethanesulfonyloxy)benzene, and 1,2,3-tris(p-toluenesulfonyloxy)benzene; and

sulfonic acid esters of N-hydroxyimides such as N-hydroxysuccinimide methanesulfonate, N-hydroxysuccinimide trifluoromethanesulfonate, N-hydroxysuccinimide ethanesulfonate, N-hydroxysuccinimide 1-propanesulfonate, N-hydroxysuccinimide 2-propanesulfonate, N-hydroxysuccinimide 1-pentanesulfonate, N-hydroxysuccinimide 1-octanesulfonate, N-hydroxysuccinimide p-toluenesulfonate, N-hydroxysuccinimide p-methoxybenzenesulfonate, N-hydroxysuccinimide 2-chloroethanesulfonate, N-hydroxysuccinimide benzenesulfonate, N-hydroxysuccinimide 2,4,6-trimethylbenzenesulfonate, N-hydroxysuccinimide 1-naphthalenesulfonate, N-hydroxysuccinimide 2-naphthalenesulfonate, N-hydroxy-2-phenylsuccinimide methanesulfonate, N-hydroxymaleimide methanesulfonate, N-hydroxymaleimide ethanesulfonate, N-hydroxy-2-phenylmaleimide methanesulfonate, N-hydroxyglutarimide methanesulfonate, N-hydroxyglutarimide benzenesulfonate, N-hydroxyphthalimide methanesulfonate, N-hydroxyphthalimide benzenesulfonate, N-hydroxyphthalimide trifluoromethanesulfonate, N-hydroxyphthalimide p-toluenesulfonate, N-hydroxynaphthalimide methanesulfonate, N-hydroxynaphthalimide benzenesulfonate, N-hydroxy-5-norbornene-2,3-dicarboxyimide methanesulfonate, N-hydroxy-5-norbornene-2,3-dicarboxyimide trifluoromethanesulfonate, and N-hydroxy-5-norbornene-2,3-dicarboxyimide p-toluenesulfonate.

Preferred among these photoacid generators are onium salts such as triphenylsulfonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium trifluoromethanesulfonate, tris(p-tert-butoxyphenyl)sulfonium trifluoromethanesulfonate, triphenylsulfonium p-toluenesulfonate, (p-tert-butoxyphenyl) diphenylsulfonium p-toluenesulfonate, tris(p-tert-butoxyphenyl)sulfonium p-toluenesulfonate, trinaphthylsulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, (2-norbornyl)methyl(2-oxocylohexyl)sulfonium trifluoromethanesulfonate, and 1,2′-naphthylcarbonylmethyltetrahydrothiophenium triflate; diazomethane derivatives such as bis(benzenesulfonyl)diazomethane, bis(p-toluenesulfonyl)diazomethane, bis(cyclohexylsulfonyl)diazomethane, bis(n-butylsulfonyl)diazomethane, bis(isobutylsulfonyl)diazomethane, bis(sec-butylsulfonyl)diazomethane, bis(n-propylsulfonyl)diazomethane, bis(isopropylsulfonyl)diazomethane, and bis(tert-butylsulfonyl) diazomethane; glyoxime derivatives such as bis-o-(p-toluenesulfonyl)-α-dimethylglyoxime and bis-o-(n-butanesulfonyl)-α-dimethylglyoxime; bissulfone derivatives such as bisnaphthylsulfonylmethane; and sulfonic acid esters of N-hydroxyimide compounds such as N-hydroxysuccinimide methanesulfonate, N-hydroxysuccinimide trifluoromethanesulfonate, N-hydroxysuccinimide 1-propanesulfonate, N-hydroxysuccinimide 2-propanesulfonate, N-hydroxysuccinimide 1-pentanesulfonate, N-hydroxysuccinimide p-toluenesulfonate, N-hydroxynaphthalimide methanesulfonate, and N-hydroxynaphthalimide benzenesulfonate.

These photoacid generators may be used singly or in combinations of two or more thereof. Onium salts are effective for improving rectangularity, while diazomethane derivatives and glyoxime derivatives are effective for reducing standing waves. The combination of an onium salt with a diazomethane or a glyoxime derivative allows for fine adjustment of the profile.

The photoacid generator is added in an amount of 0.1 to 15 parts, and especially 0.5 to 8 parts by weight, per 100 parts by weight of the base resin (all parts are by weight, hereinafter). Less than 0.1 part of the photoacid generator would provide a poor sensitivity whereas more than 15 parts of the photoacid generator would adversely affect transparency and resolution.

Organic Solvent

The organic solvent used herein may be any organic solvent in which the base resin, photoacid generator, and other components are soluble. Illustrative, non-limiting, examples of the organic solvent include ketones such as cyclohexanone and methyl-2-n-amylketone; alcohols such as 3-methoxybutanol, 3-methyl-3-methoxybutanol, 1-methoxy-2-propanol, and 1-ethoxy-2-propanol; ethers such as propylene glycol monomethyl ether, ethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monoethyl ether, propylene glycol dimethyl ether, and diethylene glycol dimethyl ether; and esters such as propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, ethyl lactate, ethyl pyruvate, butyl acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, tert-butyl acetate, tert-butyl propionate, and propylene glycol mono-tert-butyl ether acetate. These solvents may be used alone or in combinations of two or more thereof. Of the above organic solvents, it is recommended to use diethylene glycol dimethyl ether and 1-ethoxy-2-propanol because the photoacid generator serving as one of the resist components is most soluble therein, propylene glycol monomethyl ether acetate because it is a safe solvent, or a mixture thereof.

An appropriate amount of the organic solvent used is about 200 to 1,000 parts, especially about 400 to 800 parts by weight per 100 parts by weight of the base resin.

Other Polymer

To the resist composition of the invention, another polymer other than the inventive polymer comprising recurring units of formula (1a-1) and/or (1a-2) may also be added. The other polymers that can be added to the resist composition are, for example, those polymers comprising units of the following formula (R1) or (R2) and having a weight average molecular weight of about 1,000 to about 500,000, especially about 5,000 to about 100,000 although the other polymers are not limited thereto.

Herein, R⁰⁰¹ is hydrogen, methyl or CH₂CO₂R⁰⁰³. R⁰⁰² is hydrogen, methyl or CO₂R⁰⁰³. R⁰⁰³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. R⁰⁰⁴ is hydrogen or a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group. At least one of R⁰⁰⁵ to R⁰⁰⁸ represents a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group while the remaining R's independently represent hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Alternatively, R⁰⁰⁵ to R⁰⁰⁸, taken together, may form a ring, and in that event, at least one of R⁰⁰⁵ to R⁰⁰⁸ is a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰⁰⁹ is a monovalent hydrocarbon group of 3 to 15 carbon atoms containing a —CO₂— partial structure. At least one of R⁰¹⁰ to R⁰¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing a —CO₂— partial structure, while the remaining R's are independently hydrogen or straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms. R⁰¹⁰ to R⁰¹³, taken together, may form a ring, and in that event, at least one of R⁰¹⁰ to R⁰¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing a —CO₂— partial structure, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰¹⁴ is a polycyclic hydrocarbon group having 7 to 15 carbon atoms or an alkyl group containing a polycyclic hydrocarbon group. R⁰¹⁵ is an acid labile group. R⁰¹⁶ is hydrogen or methyl. R⁰¹⁷ is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms. Letter k′ is equal to 0 or 1; a1′, a2′, a3′, b1′, b2′, b3′, c1′, c2′, c3′, d1′, d2′, d3′, and e′ are numbers from 0 to less than 1, satisfying a1′+a2′+a3′+b1′+b2′+b3′+c1′+c2′+c3′+d1′+d2′+d3′+e′=1; f′, g′, h′, i′, and j′ are numbers from 0 to less than 1, satisfying f′+g′+h′+i′+j′=1. X′, y′ and z′ are integers of 0 to 3, satisfying x′+y′+z′<5 and 1≦y′+Z′.

Exemplary groups of these R's are as exemplified above for R¹ to R¹⁵.

The inventive polymer (comprising recurring units of formula (1a-1) and/or (1a-2)) and the other polymer are preferably blended in a weight ratio from 10:90 to 90:10, more preferably from 20:80 to 80:20. If the blend ratio of the inventive polymer is below this range, the resist composition would become poor in some of the desired properties. The properties of the resist composition can be adjusted by properly changing the blend ratio of the inventive polymer.

The other polymer is not limited to one type and a mixture of two or more other polymers may be added. The use of plural polymers allows for easy adjustment of resist properties.

Dissolution Regulator

To the resist composition, a dissolution regulator may be added. The dissolution regulator is a compound having on the molecule at least two phenolic hydroxyl groups, in which an average of from 0 to 100 mol % of all the hydrogen atoms on the phenolic hydroxyl groups are replaced with acid labile groups or a compound having on the molecule at least one carboxyl group, in which an average of 50 to 100 mol % of all the hydrogen atoms on the carboxyl groups are replaced with acid labile groups, both the compounds having an average molecular weight within a range of 100 to 1,000, and preferably 150 to 800.

The degree of substitution of the hydrogen atoms on the phenolic hydroxyl groups with acid labile groups is on average at least 0 mol %, and preferably at least 30 mol %, of all the phenolic hydroxyl groups. The upper limit is 100 mol %, and preferably 80 mol %. The degree of substitution of the hydrogen atoms on the carboxyl groups with acid labile groups is on average at least 50 mol %, and preferably at least 70 mol %, of all the carboxyl groups, with the upper limit being 100 mol %.

Preferable examples of such compounds having two or more phenolic hydroxyl groups or compounds having at least one carboxyl group include those of formulas (D1) to (D14) below.

In these formulas, R²⁰¹ and R²⁰² are each hydrogen or a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms; R²⁰³ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or —(R²⁰⁷)_(h)—COOH; R²⁰⁴ is —(CH₂)_(i)— (where i=2 to 10), an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R²⁰⁵ is an alkylene of 1 to 10 carbon atoms, an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R²⁰⁶ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a hydroxyl-substituted phenyl or naphthyl; R²⁰⁷ is a straight or branched alkylene of 1 to 10 carbon atoms; R²⁰⁸ is hydrogen or hydroxyl; the letter j is an integer from 0 to 5; u and h are each 0 or 1; s, t, s′, t′, s″, and t″ are each numbers which satisfy s+t=8, s′+t′=5, and s″+t″=4, and are such that each phenyl skeleton has at least one hydroxyl group; and α is a number such that the compounds of formula (D8) or (D9) have a molecular weight of from 100 to 1,000.

In the above formulas, suitable examples of R²⁰¹ and R²⁰² include hydrogen, methyl, ethyl, butyl, propyl, ethynyl, and cyclohexyl; suitable examples of R²⁰³ include the same groups as for R²⁰¹ and R²⁰², as well as —COOH and —CH₂COOH; suitable examples of R²⁰⁴ include ethylene, phenylene, carbonyl, sulfonyl, oxygen, and sulfur; suitable examples of R²⁰⁵ include methylene as well as the same groups as for R²⁰⁴; and suitable examples of R²⁰⁶ include hydrogen, methyl, ethyl, butyl, propyl, ethynyl, cyclohexyl, and hydroxyl-substituted phenyl or naphthyl.

Exemplary acid labile groups on the dissolution regulator include groups of the following general formulae (L1) to (L4), tertiary alkyl groups of 4 to 20 carbon atoms, trialkylsilyl groups in which each of the alkyls has 1 to 6 carbon atoms, and oxoalkyl groups of 4 to 20 carbon atoms.

In these formulas, R^(L01) and R^(L02) are each hydrogen or a straight, branched or cyclic alkyl having 1 to 18 carbon atoms; and R^(L03) is a monovalent hydrocarbon group of 1 to 18 carbon atoms which may contain a heteroatom (e.g., oxygen). A pair of R^(L01) and R^(L02), a pair of R^(L01) and R^(L03) or a pair of R^(L02) and R^(L03) may together form a ring, with the proviso that R^(L01), R^(L02), and R^(L03) are each a straight or branched alkylene of 1 to 18 carbon atoms when they form a ring. R^(L04) is a tertiary alkyl group of 4 to 20 carbon atoms, a trialkysilyl group in which each of the alkyls has 1 to 6 carbon atoms, an oxoalkyl group of 4 to 20 carbon atoms, or a group of the formula (L1). R^(L05) is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. R^(L06) is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. R^(L07) to R^(L16) independently represent hydrogen or monovalent hydrocarbon groups of 1 to 15 carbon atoms which may contain a hetero atom. Alternatively, R^(L07) to R^(L16), taken together, may form a ring. Each of R^(L07) to R^(L16) represents a divalent C₁-C₁₅ hydrocarbon group which may contain a hetero atom, when they form a ring. Two of R^(L07) to R^(L16) which are attached to adjoining carbon atoms may bond together directly to form a double bond. Letter y is an integer of 0 to 6. Letter m is equal to 0 or 1, n is equal to 0, 1, 2 or 3, and 2m+n is equal to 2 or 3.

The dissolution regulator may be formulated in an amount of 0 to 50 parts, preferably 5 to 50 parts, and more preferably 10 to 30 parts, per 100 parts of the base resin, and may be used singly or as a mixture of two or more thereof. Less than 5 parts of the dissolution regulator may fail to yield an improved resolution, whereas the use of more than 50 parts would lead to slimming of the patterned film, and thus a decline in resolution.

The dissolution regulator can be synthesized by introducing acid labile groups into a compound having phenolic hydroxyl or carboxyl groups in accordance with an organic chemical formulation.

Basic Compound

In the resist composition of the invention, a basic compound may be blended. A suitable basic compound used herein is a compound capable of suppressing the rate of diffusion when the acid generated by the photoacid generator diffuses within the resist film. The inclusion of this type of basic compound holds down the rate of acid diffusion within the resist film, resulting in better resolution. In addition, it suppresses changes in sensitivity following exposure, thus reducing substrate and environment dependence, as well as improving the exposure latitude and the pattern profile.

Examples of basic compounds include primary, secondary, and tertiary aliphatic amines, mixed amines, aromatic amines, heterocyclic amines, carboxyl group-bearing nitrogenous compounds, sulfonyl group-bearing nitrogenous compounds, hydroxyl group-bearing nitrogenous compounds, hydroxyphenyl group-bearing nitrogenous compounds, alcoholic nitrogenous compounds, amide derivatives, and imide derivatives.

Examples of suitable primary aliphatic amines include ammonia, methylamine, ethylamine, n-propylamine, isopropylamine, n-butylamine, iso-butylamine, sec-butylamine, tert-butylamine, pentylamine, tert-amylamine, cyclopentylamine, hexylamine, cyclohexylamine, heptylamine, octylamine, nonylamine, decylamine, dodecylamine, cetylamine, methylenediamine, ethylenediamine, and tetraethylenepentamine. Examples of suitable secondary aliphatic amines include dimethylamine, diethylamine, di-n-propylamine, di-iso-propylamine, di-n-butylamine, di-iso-butylamine, di-sec-butylamine, dipentylamine, dicyclopentylamine, dihexylamine, dicyclohexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, didodecylamine, dicetylamine, N,N-dimethylmethylenediamine, N,N-dimethylethylenediamine, and N,N-dimethyltetraethylenepentamine. Examples of suitable tertiary aliphatic amines include trimethylamine, triethylamine, tri-n-propylamine, tri-iso-propylamine, tri-n-butylamine, tri-iso-butylamine, tri-sec-butylamine, tripentylamine, tricyclopentylamine, trihexylamine, tricyclohexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, tridodecylamine, tricetylamine, N,N,N′,N′-tetramethylmethylenediamine, N,N,N′,N′-tetramethylethylenediamine, and N,N,N′,N′-tetramethyltetraethylenepentamine.

Examples of suitable mixed amines include dimethylethylamine, methylethylpropylamine, benzylamine, phenethylamine, and benzyldimethylamine. Examples of suitable aromatic and heterocyclic amines include aniline derivatives (e.g., aniline, N-methylaniline, N-ethylaniline, N-propylaniline, N,N-dimethylaniline, 2-methylaniline, 3-methylaniline, 4-methylaniline, ethylaniline, propylaniline, trimethylaniline, 2-nitroaniline, 3-nitroaniline, 4-nitroaniline, 2,4-dinitroaniline, 2,6-dinitroaniline, 3,5-dinitroaniline, and N,N-dimethyltoluidine), diphenyl(p-tolyl)amine, methyldiphenylamine, triphenylamine, phenylenediamine, naphthylamine, diaminonaphthalene, pyrrole derivatives (e.g., pyrrole, 2H-pyrrole, 1-methylpyrrole, 2,4-dimethylpyrrole, 2,5-dimethylpyrrole, and N-methylpyrrole), oxazole derivatives (e.g., oxazole and isooxazole), thiazole derivatives (e.g., thiazole and isothiazole), imidazole derivatives (e.g., imidazole, 4-methylimidazole, and 4-methyl-2-phenylimidazole), pyrazole derivatives, furazan derivatives, pyrroline derivatives (e.g., pyrroline and 2-methyl-1-pyrroline), pyrrolidine derivatives (e.g., pyrrolidine, N-methylpyrrolidine, pyrrolidinone, and N-methylpyrrolidone), imidazoline derivatives, imidazolidine derivatives, pyridine derivatives (e.g., pyridine, methylpyridine, ethylpyridine, propylpyridine, butylpyridine, 4-(1-butylpentyl)pyridine, dimethylpyridine, trimethylpyridine, triethylpyridine, phenylpyridine, 3-methyl-2-phenylpyridine, 4-tert-butylpyridine, diphenylpyridine, benzylpyridine, methoxypyridine, butoxypyridine, dimethoxypyridine, 1-methyl-2-pyridine, 4-pyrrolidinopyridine, 1-methyl-4-phenylpyridine, 2-(1-ethylpropyl)pyridine, aminopyridine, and dimethylaminopyridine), pyridazine derivatives, pyrimidine derivatives, pyrazine derivatives, pyrazoline derivatives, pyrazolidine derivatives, piperidine derivatives, piperazine derivatives, morpholine derivatives, indole derivatives, isoindole derivatives, 1H-indazole derivatives, indoline derivatives, quinoline derivatives (e.g., quinoline and 3-quinolinecarbonitrile), isoquinoline derivatives, cinnoline derivatives, quinazoline derivatives, quinoxaline derivatives, phthalazine derivatives, purine derivatives, pteridine derivatives, carbazole derivatives, phenanthridine derivatives, acridine derivatives, phenazine derivatives, 1,10-phenanthroline derivatives, adenine derivatives, adenosine derivatives, guanine derivatives, guanosine derivatives, uracil derivatives, and uridine derivatives.

Examples of suitable carboxyl group-bearing nitrogenous compounds include aminobenzoic acid, indolecarboxylic acid, and amino acid derivatives (e.g. nicotinic acid, alanine, alginine, aspartic acid, glutamic acid, glycine, histidine, isoleucine, glycylleucine, leucine, methionine, phenylalanine, threonine, lysine, 3-aminopyrazine-2-carboxylic acid, and methoxyalanine). Examples of suitable sulfonyl group-bearing nitrogenous compounds include 3-pyridinesulfonic acid and pyridinium p-toluenesulfonate. Examples of suitable hydroxyl group-bearing nitrogenous compounds, hydroxyphenyl group-bearing nitrogenous compounds, and alcoholic nitrogenous compounds include 2-hydroxypyridine, aminocresol, 2,4-quinolinediol, 3-indolemethanol hydrate, monoethanolamine, diethanolamine, triethanolamine, N-ethyldiethanolamine, N,N-diethylethanolamine, triisopropanolamine, 2,21-iminodiethanol, 2-aminoethanol, 3-amino-1-propanol, 4-amino-1-butanol, 4-(2-hydroxyethyl) morpholine, 2-(2-hydroxyethyl)pyridine, 1-(2-hydroxyethyl) piperazine, 1-[2-(2-hydroxyethoxy)ethyl]-piperazine, piperidine ethanol, 1-(2-hydroxyethyl)pyrrolidine, 1-(2-hydroxyethyl)-2-pyrrolidinone, 3-piperidino-1,2-propanediol, 3-pyrrolidino-1,2-propanediol, 8-hydroxyjulolidine, 3-quinuclidinol, 3-tropanol, 1-methyl-2-pyrrolidine ethanol, 1-aziridine ethanol, N-(2-hydroxyethyl)phthalimide, and N-(2-hydroxyethyl)isonicotinamide. Examples of suitable amide derivatives include formamide, N-methylformamide, N,N-dimethylformamide, acetamide, N-methylacetamide, N,N-dimethylacetamide, propionamide, and benzamide. Suitable imide derivatives include phthalimide, succinimide, and maleimide.

In addition, basic compounds of the following general formula (B1) may also be included alone or in admixture.

N(X)_(n)(Y)_(3−n)  B1

In the formula, n is equal to 1, 2 or 3; Y is independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 20 carbon atoms which may contain a hydroxyl group or ether; and X is independently selected from groups of the following general formulas (X1) to (X3), and two or three X's may bond together to form a ring.

In the formulas, R³⁰⁰, R³⁰² and R³⁰⁵ are independently straight or branched alkylene groups of 1 to 4 carbon atoms; R³⁰¹ and R³⁰⁴ are independently hydrogen, straight, branched or cyclic alkyl groups of 1 to 20 carbon atoms, which may contain at least one hydroxyl group, ether, ester or lactone ring; and R³⁰³ is a single bond or a straight or branched alkylene group of 1 to 4 carbon atoms.

Illustrative examples of the compounds of formula (B1) include tris(2-methoxymethoxyethyl)amine, tris{2-(methoxyethoxy)ethyl}amine, tris{2-(2-methoxyethoxymethoxy)ethyl}amine, tris{2-(1-methoxyethoxy)ethyl}amine, tris{2-(1-ethoxyethoxy)ethyl}amine, tris{2-(1-ethoxy-propoxy) ethyl}amine, tris[2-{2-(2-hydroxyethoxy)ethoxy}-ethyl]amine, 4,7,13,16,21,24-hexaoxa-1,10-diazabicyclo-[8.8.8]hexacosane, 4,7,13,18-tetraoxa-1,10-diazabicyclo-[8.5.5]eicosane, 1,4,10,13-tetraoxa-7,16-diazabicyclooctadecane, 1-aza-12-crown-4,1-aza-15-crown-5, 1-aza-18-crown-6, tris(2-formyloxyethyl)amine, tris(2-acetoxyethyl)amine, tris(2-propionyloxyethyl)amine, tris(2-butyryloxyethyl) amine, tris(2-isobutyryloxyethyl)amine, tris(2-valeryloxyethyl)amine, tris(2-pivaloyloxyethyl)amine, N,N-bis(2-acetoxyethyl)-2-(acetoxyacetoxy)ethylamine, tris(2-methoxycarbonyloxyethyl)amine, tris(2-tert-butoxycarbonyloxyethyl) amine, tris[2-(2-oxopropoxy)ethyl]amine, tris[2-(methoxycarbonylmethyl)oxyethyl]amine, tris[2-(tert-butoxycarbonylmethyloxy)ethyl]amine, tris[2-(cyclohexyloxycarbonylmethyloxy)ethyl]amine, tris(2-methoxycarbonylethyl)amine, tris(2-ethoxycarbonylethyl)amine, N,N-bis(2-hydroxyethyl)-2-(methoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(methoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(ethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(ethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-methoxyethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-methoxyethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-hydroxyethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-acetoxyethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-[(methoxycarbonyl)methoxycarbonyl]ethylamine, N,N-bis(2-acetoxyethyl)-2-[(methoxycarbonyl)methoxycarbonyl]ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-oxopropoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-oxopropoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(tetrahydrofurfuryloxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(tetrahydrofurfuryloxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-[(2-oxotetrahydrofuran-3-yl)oxycarbonyl]ethylamine, N,N-bis(2-acetoxyethyl)-2-[(2-oxotetrahydrofuran-3-yl)oxycarbonyl]-ethylamine, N,N-bis(2-hydroxyethyl)-2-(4-hydroxybutoxycarbonyl)ethylamine, N,N-bis(2-formyloxyethyl)-2-(4-formyloxybutoxycarbonyl)ethylamine, N,N-bis(2-formyloxyethyl)-2-(2-formyloxyethoxycarbonyl)ethylamine, N,N-bis(2-methoxyethyl)-2-(methoxycarbonyl)ethylamine, N-(2-hydroxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-acetoxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-hydroxyethyl)-bis[2-(ethoxycarbonyl)ethyl]amine, N-(2-acetoxyethyl)-bis[2-(ethoxycarbonyl)ethyl]amine, N-(3-hydroxy-1-propyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(3-acetoxy-1-propyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-methoxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-butyl-bis[2-(methoxycarbonyl)ethyl]amine, N-butyl-bis[2-(2-methoxyethoxycarbonyl)ethyl]amine, N-methyl-bis(2-acetoxyethyl)amine, N-ethyl-bis(2-acetoxyethyl)amine, N-methyl-bis(2-pivaloyloxyethyl)amine, N-ethyl-bis[2-(methoxycarbonyloxy)ethyl]amine, N-ethyl-bis[2-(tert-butoxycarbonyloxy)ethyl]amine, tris(methoxycarbonylmethyl)amine, tris(ethoxycarbonylmethyl)amine, N-butyl-bis(methoxycarbonylmethyl)amine, N-hexyl-bis(methoxycarbonylmethyl)amine, and β-(diethylamino)-δ-valerolactone.

The basic compound is preferably formulated in an amount of 0.001 to 10 parts, and especially 0.01 to 1 part, per part of the photoacid generator. Less than 0.001 part of the basic compound fails to achieve the desired effects thereof, while the use of more than 10 parts would result in too low a sensitivity and resolution.

Other Components

In the resist composition, a compound bearing a ≡C—COOH group in a molecule may be blended. Exemplary, non-limiting compounds bearing a ≡C—COOH group include one or more compounds selected from Groups I and II below. Including this compound improves the PED stability of the resist and ameliorates edge roughness on nitride film substrates.

Group I:

Compounds in which some or all of the hydrogen atoms on the phenolic hydroxyl groups of the compounds of general formulas (A1) to (A10) below have been replaced with —R⁴⁰¹—COOH (wherein R⁴⁰¹ is a straight or branched alkylene of 1 to 10 carbon atoms), and in which the molar ratio C/(C+D) of phenolic hydroxyl groups (C) to ≡C—COOH groups (D) in the molecule is from 0.1 to 1.0.

In these formulas, R⁴⁰⁸ is hydrogen or methyl; R⁴⁰² and R⁴⁰³ are each hydrogen or a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms; R⁴⁰⁴ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a —(R⁴⁰⁹)_(h)—COOR′ group (R′ being hydrogen or —R⁴⁰⁹—COOH); R⁴⁰⁵ is —(CH₂)_(i)— (wherein i is 2 to 10), an arylene of 6 to 10 carbon 10 atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R⁴⁰⁶ is an alkylene of 1 to 10 carbon atoms, an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R⁴⁰⁷ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a hydroxyl-substituted phenyl or naphthyl; R⁴⁰⁹ is a straight or branched alkylene of 1 to 10 carbon atoms; R⁴¹⁰ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a —R⁴¹¹—COOH group; R⁴¹¹ is a straight or branched alkylene of 1 to 10 carbon atoms; the letter j is an integer from 0 to 5; u and h are each 0 or 1; s1, t1, s2, t2, s3, t3, s4, and t4 are each numbers which satisfy s1+t1=8, s2+t2=5, s3+t3=4, and s4+t4=6, and are such that each phenyl skeleton has at least one hydroxyl group; κ is a number such that the compound of formula (A6) may have a weight average molecular weight of 1,000 to 5,000; and λ is a number such that the compound of formula (A7) may have a weight average molecular weight of 1,000 to 10,000.

Group II:

Compounds of general formulas (A11) to (A15) below.

In these formulas, R⁴⁰², R⁴⁰³, and R⁴¹¹ are as defined above; R⁴¹² is hydrogen or hydroxyl; s5 and t5 are numbers which satisfy s5≧0, t5≧0, and s5+t5=5; and h′ is equal to 0 or 1.

Illustrative, non-limiting examples of the compound bearing a ≡C—COOH group include compounds of the general formulas AI-1 to AI-14 and AII-1 to AII-10 below.

In the above formulas, R″ is hydrogen or a CH₂COOH group such that the CH₂COOH group accounts for 10 to 100 mol % of R″ in each compound, α and κ are as defined above.

The compound bearing a ≡C—COOH group within the molecule may be used singly or as combinations of two or more thereof.

The compound bearing a ≡C—COOH group within the molecule is added in an amount ranging from 0 to 5 parts, preferably 0.1 to 5 parts, more preferably 0.1 to 3 parts, further preferably 0.1 to 2 parts, per 100 parts of the base resin. More than 5 parts of the compound can reduce the resolution of the resist composition.

The resist composition of the invention may additionally include an acetylene alcohol derivative for the purpose of enhancing the shelf stability. Preferred acetylene alcohol derivatives are those having the general formula (S1) or (S2) below.

In the formulas, R⁵⁰¹, R⁵⁰², R⁵⁰³, R⁵⁰⁴, and R⁵⁰⁵ are each hydrogen or a straight, branched, or cyclic alkyl of 1 to 8 carbon atoms; and X and Y are each 0 or a positive number, satisfying 0≦X≦30, 0≦Y≦30, and 0≦X+Y≦40.

Preferable examples of the acetylene alcohol derivative include Surfynol 61, Surfynol 82, Surfynol 104, Surfynol 104E, Surfynol 104H, Surfynol 104A, Surfynol TG, Surfynol PC, Surfynol 440, Surfynol 465, and Surfynol 485 from Air Products and Chemicals Inc., and Surfynol E1004 from Nisshin Chemical Industry K.K.

The acetylene alcohol derivative is preferably added in an amount of 0.01 to 2% by weight, and more preferably 0.02 to 1% by weight, per 100% by weight of the resist composition. Less than 0.01% by weight would be ineffective for improving coating characteristics and shelf stability, whereas more than 2% by weight would result in a resist having a low resolution.

The resist composition of the invention may include, as an optional ingredient, a surfactant which is commonly used for improving the coating characteristics. Optional ingredients may be added in conventional amounts so long as this does not compromise the objects of the invention.

Nonionic surfactants are preferred, examples of which include perfluoroalkylpolyoxyethylene ethanols, fluorinated alkyl esters, perfluoroalkylamine oxides, perfluoroalkyl EO-addition products, and fluorinated organosiloxane compounds. Useful surfactants are commercially available under the trade names Florade FC-430 and FC-431 from Sumitomo 3M K.K., Surflon S-141 and S-145 from Asahi Glass K.K., Unidine DS-401, DS-403 and DS-451 from Daikin Industry K.K., Megaface F-8151 from Dai-Nippon Ink & Chemicals K.K., and X-70-092 and X-70-093 from Shin-Etsu Chemical Co., Ltd. Preferred surfactants are Florade FC-430 from Sumitomo 3M K.K. and X-70-093 from Shin-Etsu Chemical Co., Ltd.

Pattern formation using the resist composition of the invention may be carried out by a known lithographic technique. For example, the resist composition is applied onto a substrate such as a silicon wafer by spin coating or the like to form a resist film having a thickness of 0.3 to 2.0 μm, which is then pre-baked on a hot plate at 60 to 150° C. for 1 to 10 minutes, and preferably at 80 to 130° C. for 1 to 5 minutes. A patterning mask having the desired pattern is then placed over the resist film, and the film exposed through the mask to an electron beam or to high-energy radiation such as deep-UV rays, an excimer laser, or x-rays in a dose of about 1 to 200 mJ/cm², and preferably about 10 to 100 mJ/cm², then post-exposure baked (PEB) on a hot plate at 60 to 150° C. for 1 to 5 minutes, and preferably at 80 to 130° C. for 1 to 3 minutes. Finally, development is carried out using as the developer an aqueous alkali solution, such as a 0.1 to 5% (preferably 2 to 3%) aqueous solution of tetramethylammonium hydroxide (TMAH), this being done by a conventional method such as dipping, puddling, or spraying for a period of 0.1 to 3 minutes, and preferably 0.5 to 2 minutes. These steps result in the formation of the desired pattern on the substrate. Of the various types of high-energy radiation that may be used, the resist composition of the invention is best suited to fine pattern formation with, in particular, deep-UV rays having a wavelength of 248 to 193 nm, an excimer laser, x-rays, or an electron beam. The desired pattern may not be obtainable outside the upper and lower limits of the above range.

The resist composition comprising the polymer as a base resin lends itself to micropatterning with electron beams or deep-UV rays since it is sensitive to high-energy radiation and has excellent sensitivity, resolution, and etching resistance. Especially because of the minimized absorption at the exposure wavelength of an ArF or KrF excimer laser, a finely defined pattern having sidewalls perpendicular to the substrate can easily be formed.

EXAMPLE

Synthesis Examples and Examples are given below by way of illustration and not by way of limitation.

Synthesis Examples

Ester compounds and polymers containing the same were synthesized according to the following formulation.

Synthesis Example 1-1

Synthesis of Monomer 1

In 500 ml of diethyl ether was dissolved 168.0 g of chlorocyclohexane. Below 60° C., this reaction mixture was added dropwise to 26.4 g of metallic magnesium over one hour. After agitation was continued for 2 hours at room temperature, 84.0 g of cyclopentanone was added dropwise over 45 minutes to the reaction mixture which was kept below 65° C. After agitation was continued for one hour at room temperature, the reaction solution was worked up in a conventional manner. The resulting oily substance was distilled in vacuum, collecting 97.3 g of 1-cyclohexylcyclopentanol. The yield was 57.9%.

In 1 liter of methylene chloride was dissolved 92.4 g of 1-cyclohexylcyclopentanol. To the solution below −20° C, 74.3 g of acrylic chloride was added dropwise over 10 minutes. To the reaction mixture, 1.0 g of 4-(N,N-dimethylamino)pyridine was added and then, 125.0 g of triethylamine was added dropwise over one hour and below −20° C. This reaction mixture was agitated for 15 hours at room temperature and subjected to conventional post-treatment, obtaining about 130 g of an oily substance. This was used in the subsequent reaction without purification.

The oily substance obtained in the above step was dissolved in 300 ml of benzene. To this solution below 10° C., 72.6 g of cyclopentadiene was added dropwise over 10 minutes. The reaction mixture was agitated for 17 hours at room temperature, then for one hour at 70° C., and concentrated in vacuum. Vacuum distillation (170° C./0.2 Torr) of the resulting oily substance yielded 106.6 g of 1-cyclohexylcyclopentyl 5-norbornene-2-carboxylate (designated Monomer 1). The yield was 67.3%.

FIG. 1 shows the spectrum of Monomer 1 by ¹H-NMR (CDCl₃, 270 MHz).

Synthesis Examples 1-2 to 1-8

Synthesis of Monomers 2 to 8

Monomers 2 to 8 were synthesized by the same procedure as above or a well-known procedure.

Synthesis Example 2-1

Synthesis of Polymer 1

In 1 liter of tetrahydrofuran, 72.0 g of Monomer 1 and 24.5 g of maleic anhydride were dissolved, and 1.8 g of 2,2′-azobisisobutyronitrile added. After agitation was continued for 15 hours at 60° C., the reaction solution was concentrated in vacuum. The residue was dissolved in 400 ml of tetrahydrofuran, which was, in turn, added dropwise to 10 liters of n-hexane. The resulting solids were collected by filtration, washed with 10 liters of n-hexane, and dried in vacuum at 40° C. for 6 hours, obtaining 53.6 g of a polymer, designated Polymer 1. The yield was 55.5%.

Synthesis Examples 2-2 to 2-18

Synthesis of Polymers 2 to 18

Polymers 2 to 18 were synthesized by the same procedure as above or a well-known procedure.

Example I

Resist compositions were formulated using inventive polymers and examined for resolution upon KrF excimer laser exposure.

Examples I-1 to I-28

Evaluation of Resist Resolution

Resist compositions were prepared by using Polymers 1 to 18 as the base resin, and dissolving the polymer, a photoacid generator (designated as PAG 1 and 2), a dissolution regulator (designated as DRR 1 to 4), a basic compound, and a compound having a ≡C—COOH group in the molecule (ACC 1 and 2) in a solvent in accordance with the formulation shown in Tables 1 and 2. These compositions were each filtered through a Teflon filter (pore diameter 0.2 μm), thereby giving resist solutions.

The solvents and basic compounds used are as follows. It is noted that the solvents contained 0.01% by weight of surfactant Florade FC-430 (Sumitomo 3M).

PGMEA: propylene glycol methyl ether acetate

CyHO: cyclohexanone

TBA: tributylamine

TEA: triethanolamine

TMMEA: trismethoxymethoxyethylamine

TMEMEA: trismethoxyethoxymethoxyethylamine

These resist solutions were spin-coated onto silicon wafers, then baked on a hot plate at 110° C. for 90 seconds to give resist films having a thickness of 0.5 μm. The resist films were exposed using an KrF excimer laser stepper (Nikon Corporation; NA 0.5), then baked (PEB) at 110° C. for 90 seconds, and developed with a solution of 2.38% TMAH in water, thereby giving positive patterns.

The resulting resist patterns were evaluated as described below. First, the sensitivity (Eth, mJ/cm²) was determined. Next, the optimal dose (Eop, mJ/cm²) was defined as the dose which provides a 1:1 resolution at the top and bottom of a 0.30 μm line-and-space pattern, and the resolution of the resist under evaluation was defined as the minimum line width (μm) of the lines and spaces that separated at this dose. The shape of the resolved resist pattern was examined under a scanning electron microscope.

The composition and test results of the resist materials are shown in Tables 1 and 2.

Comparative Example

For comparison purposes, resist compositions were formulated and examined for resolution upon KrF excimer laser exposure.

Comparative Examples 1 to 4

Resist compositions were prepared as in Example I except that Polymers 19 and 20 shown below were used as the base resin, in accordance with the formulation shown in Table 3.

These resist materials were similarly evaluated. The composition and test results of these resist materials are shown in Table 3.

TABLE 1 Photoacid Dissolution Basic Optimum Base resin generator regulator compound Solvent dose Resolution Example (pbw) (pbw) (pbw) (pbw) (pbw) (mJ/cm²) (μm) Shape I-1 Polymer 1 PAG 1 TBA PGMEA 24.0 0.22 rectangular (80) (1) (0.078) (480) I-2 Polymer 2 PAG 1 TBA PGMEA 20.0 0.22 rectangular (80) (1) (0.078) (480) I-3 Polymer 3 PAG 1 TBA PGMEA 23.0 0.22 rectangular (80) (1) (0.078) (480) I-4 Polymer 4 PAG 1 TBA PGMEA 21.5 0.22 rectangular (80) (1) (0.078) (480) I-5 Polymer 5 PAG 1 TBA PGMEA 24.5 0.22 rectangular (80) (1) (0.078) (480) I-6 Polymer 6 PAG 1 TBA PGMEA 19.5 0.22 rectangular (80) (1) (0.078) (480) I-7 Polymer 7 PAG 1 TBA PGMEA 25.0 0.22 rectangular (80) (1) (0.078) (480) I-8 Polymer 8 PAG 1 TBA PGMEA 22.5 0.22 rectangular (80) (1) (0.078) (480) I-9 Polymer 9 PAG 1 TBA PGMEA 22.0 0.22 rectangular (80) (1) (0.078) (480) I-10 Polymer 10 PAG 1 TBA PGMEA 25.5 0.22 rectangular (80) (1) (0.078) (480) I-11 Polymer 11 PAG 1 TBA PGMEA 22.5 0.22 rectangular (80) (1) (0.078) (480) I-12 Polymer 12 PAG 1 TBA PGMEA 22.5 0.22 rectangular (80) (1) (0.078) (480) I-13 Polymer 13 PAG 1 TBA CyHO 18.0 0.22 rectangular (80) (1) (0.078) (640) I-14 Polymer 14 PAG 1 TBA CyHO 16.5 0.22 rectangular (80) (1) (0.078) (640) I-15 Polymer 15 PAG 1 TBA CyHO 16.0 0.22 rectangular (80) (1) (0.078) (640) I-16 Polymer 16 PAG 1 TBA CyHO 21.5 0.22 rectangular (80) (1) (0.078) (640) I-17 Polymer 17 PAG 1 TBA CyHO 20.5 0.22 rectangular (80) (1) (0.078) (640) I-18 Polymer 18 PAG 1 TBA CyHO 20.0 0.22 rectangular (80) (1) (0.078) (640) I-19 Polymer 12 PAG 2 TBA PGMEA 23.0 0.22 rectangular (80) (1) (0.078) (480) I-20 Polymer 12 PAG 2 TBA PGMEA 22.0 0.20 rectangular (80) (1) (0.063) (480)

TABLE 2 Photoacid Dissolution Basic Optimum Base resin generator regulator compound Solvent dose Resolution Example (pbw) (pbw) (pbw) (pbw) (pbw) (mJ/cm²) (μm) Shape I-21 Polymer 12 PAG 2 TMMEA PGMEA 22.0 0.20 rectangular (80) (1) (0.118) (480) I-22 Polymer 12 PAG 2 TMEMEA PGMEA 22.5 0.22 rectangular (80) (1) (0.173) (480) I-23 Polymer 7 PAG 2 DRR 1 TEA PGMEA 22.0 0.24 rectangular (70) (1) (10) (0.063) (480) I-24 Polymer s7 PAG 2 DRR 2 TEA PGMEA 23.5 0.22 rectangular (70) (1) (10) (0.063) (480) I-25 Polymer 7 PAG 2 DRR 3 TEA PGMEA 26.0 0.22 rectangular (70) (1) (10) (0.063) (480) I-26 Polymer 7 PAG 2 DRR 4 TEA PGMEA 24.5 0.20 rectangular (70) (1) (10) (0.063) (480) I-27 Polymer 7 PAG 2 ACC 1 TEA PGMEA 23.0 0.22 rectangular (80) (1) (4) (0.063) (480) I-28 Polymer 7 PAG 2 ACC 2 TEA PGMEA 24.0 0.22 rectangular (80) (1) (4) (0.063) (480)

TABLE 3 Compar- Photoacid Dissolution Basic Optimum ative Base resin generator regulator compound Solvent dose Resolution Example (pbw) (pbw) (pbw) (pbw) (pbw) (mJ/cm²) (μm) Shape 1 Polymer 19 PAG 1 TEA PGMEA — — not (80) (1) (0.078) (480) resolved 2 Polymer 20 PAG 1 TEA PGMEA 29.0 0.28 T-top (80) (1) (0.078) (480) 3 Polymer 19 PAG 1 DRR 4 TEA PGMEA 27.0 0.26 forward (70) (1) (10) (0.063) (480) tapered 4 Polymer 20 PAG 1 DRR 4 TEA PGMEA 26.0 0.26 forward (70) (1) (10) (0.063) (480) tapered

It is seen from Tables 1 to 3 that the resist compositions within the scope of the invention have a high sensitivity and resolution upon KrF excimer laser exposure, as compared with prior art compositions.

Example II

Resist compositions were formulated using inventive polymers and examined for resolution upon ArF excimer laser exposure.

Examples II-1 to II-2

Evaluation of Resist Resolution

Resist compositions were prepared as in Example I in accordance with the formulation shown in Table 4.

The resulting resist solutions were spin-coated onto silicon wafers, then baked on a hot plate at 110° C. for 90 seconds to give resist films having a thickness of 0.5 μm. The resist films were exposed using an ArF excimer laser stepper (Nikon Corporation; NA 0.55), then baked (PEB) at 110° C. for 90 seconds, and developed with a solution of 2.38% TMAH in water, thereby giving positive patterns.

The resulting resist patterns were evaluated as described below. First, the sensitivity (Eth, mJ/cm²) was determined. Next, the optimal dose (Eop, mJ/cm²) was defined as the dose which provides a 1:1 resolution at the top and bottom of a 0.25 μm line-and-space pattern, and the resolution of the resist under evaluation was defined as the minimum line width (μm) of the lines and spaces that separated at this dose. The shape of the resolved resist pattern was examined under a scanning electron microscope.

The composition and test results of the resist materials are shown in Table 4.

TABLE 4 Photoacid Dissolution Basic Optimum Base resin generator regulator compound Solvent dose Resolution Example (pbw) (pbw) (pbw) (pbw) (pbw) (mJ/cm²) (μm) Shape II-1 Polymer 1 PAG 1 TEA PGMEA 17.0 0.16 rectangular (80) (1) (0.078) (480) II-2 Polymer 1 PAG 1 DRR 4 TEA PGMEA 15.5 0.16 rectangular (70) (1) (10) (0.063) (480)

It is seen from Table 4 that the resist compositions within the scope of the invention have a high sensitivity and resolution upon ArF excimer laser exposure.

Japanese Patent Application No. 2000-119410 is incorporated herein by reference.

Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims. 

What is claimed is:
 1. An ester compound of the following general formula (1):

wherein R¹ is hydrogen, methyl or CH₂CO₂R³, R² is hydrogen, methyl or CO₂R³, R³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, k is 0 or 1, Z is a divalent hydrocarbon group of 2 to 20 carbon atoms which forms a bridged ring with the carbon atom and which may contain a hetero atom, m is 0 or 1, n is 0, 1, 2 or 3, and 2 m+n is 2 or
 3. 2. A method for preparing a polymer comprising the step of effecting radical polymerization, anionic polymerization or coordination polymerization between an ester compound according to claim 1 and another compound having a carbon-to-carbon double bond.
 3. A compound according to claim 1, wherein R¹ is hydrogen, methyl or CH₂CO₂R³, and wherein R³ is methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl or butyladamantyl.
 4. A compound according to claim 1, wherein R² is hydrogen, methyl or CO₂R³, and wherein R³ is methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl or butyladamantyl.
 5. A compound according to claim 1, wherein R³ is methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl or butyladamantyl.
 6. A compound according to claim 1, wherein Z is bicyclo[2.2.1]heptane, bicyclo[2.2.2]octane, bicyclo[4.4.0]decane or tricyclo[5.2.1.0^(2,6)]decane, which in each case is unsubstituted or substituted by alkyl, hydroxy, alkoxy, acyloxy, alkylcarbonyl, hydroxycarbonyl, alkoxycarbonyl or oxo.
 7. A compound according to claim 6, wherein Z is bicyclo[2.2.1]heptane, bicyclo[2.2.2]octane, bicyclo[4.4.0]decane or tricyclo[5.2.1.0^(2,6)]decane.
 8. A polymer comprising recurring units of the following general formula (1a-1) and/or (1a-2) derived from an ester compound of the general formula (1), and having a weight average molecular weight of 1,000 to 500,000,

wherein R¹, R², Z, k, m and n are as defined above.
 9. A resist composition comprising the polymer of claim
 8. 10. A process for forming a resist pattern comprising the steps of: applying the resist composition of claim 9, onto a substrate to form a coating, heat treating the coating and then exposing it to high-energy radiation or electron beams through a photo mask, and optionally heat treating the exposed coating and developing it with a developer.
 11. A resist composition comprising the polymer of claim 8, a photoacid generator, and an organic solvent.
 12. The polymer of claim 8 further comprising recurring units of at least one of the following formulas (2a) to (10a):

wherein R¹, R² and k are as defined above, R⁴ is hydrogen or a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms, at least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms, and the remainders are independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, or R⁵ to R⁸, taken together, may form a ring, and when they form a ring, at least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing divalent hydrocarbon group of 1 to 15 carbon atoms, and the remainders are independently a single bond or a straight, branched or cyclic alkylene group of 1 to 15 carbon atoms, R⁹ is a monovalent hydrocarbon group of 3 to 15 carbon atoms containing a —CO₂— partial structure, at least one of R¹⁰ to R¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing a —CO₂— partial structure, and the remainders are independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, or R¹⁰ to R¹³, taken together, may form a ring, and when they form a ring, at least one of R¹⁰ to R¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing a —CO₂— partial structure, and the remainders are independently a single bond or a straight, branched or cyclic alkylene group of 1 to 15 carbon atoms, R¹⁴ is a polycyclic hydrocarbon group of 7 to 15 carbon atoms or an alkyl group containing such a polycyclic hydrocarbon group, R¹⁵ is an acid labile group, X is —CH₂— or —O—, and Y is —O— or —(NR¹⁶)— wherein R¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms.
 13. A polymer according to claim 12, wherein R⁴ is H, carboxyethyl, carboxybutyl, carboxycyclopentyl, carboxycyclohexyl, carboxynorbornyl, carboxyadamantyl, hydroxyethyl, hydroxybutyl, hydroxycyclopentyl, hydroxycyclohexyl, hydroxynorbornyl, or hydroxyadamantyl.
 14. A polymer according to claim 12, wherein at least one of R⁵ to R⁸ is a carboxyl or hydroxyl-containing monovalent hydrocarbon group of 1 to 15 carbon atoms, and the remainder of R⁵ to R⁸ are each independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms.
 15. A polymer according to claim 14, wherein at least one of R⁵ to R⁸ is carboxy, carboxymethyl, carboxyethyl, carboxybutyl, hydroxymethyl, hydroxyethyl, hydroxybutyl, 2-carboxyethoxycarbonyl, 4-carboxybutoxycarbonyl, 2-hydroxyethoxycarbonyl, 4-hydroxybutoxycarbonyl, carboxycyclopentyloxycarbonyl, carboxycyclohexyloxycarbonyl, carboxynorbornyloxycarbonyl, carboxyadamantyloxycarbonyl, hydroxycyclopentyloxycarbonyl, hydroxycyclohexyloxycarbonyl, hydroxynorbornyloxycarbonyl, or hydroxyadamantyloxycarbonyl, and the remainder of R⁵ to R⁸ are each independently H, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl or butyladamantyl.
 16. A polymer according to claim 12, wherein at least one of R⁵ to R⁸ is at least a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, and the remainder of R⁵ to R⁸ are each independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms.
 17. A polymer according to claim 16, wherein at least one of R⁵ to R⁸ is a divalent group corresponding to a carboxyl or hydroxyl-bearing monovalent hydrocarbon group with one hydrogen atom eliminated, wherein said carboxyl or hydroxyl-bearing monovalent hydrocarbon group is selected from carboxy, carboxymethyl, carboxyethyl, carboxybutyl, hydroxymethyl, hydroxyethyl, hydroxybutyl, 2-carboxyethoxycarbonyl, 4-carboxybutoxycarbonyl, 2-hydroxyethoxycarbonyl, 4-hydroxybutoxycarbonyl, carboxycyclopentyloxycarbonyl, carboxycyclohexyloxycarbonyl, carboxynorbornyloxycarbonyl, carboxyadamantyloxycarbonyl, hydroxycyclopentyloxycarbonyl, hydroxycyclohexyloxycarbonyl, hydroxynorbornyloxycarbonyl, and hydroxyadamantyloxycarbonyl; and the remainder of R⁵ to R⁸ are each independently a divalent group corresponding to a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms with one hydrogen atom eliminated, wherein said alkyl group is selected from methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl and butyladamantyl.
 18. A polymer according to claim 12, wherein R⁹ is 2-oxooxolan-3-yl, 4,4-dimethyl-2-oxooxolan-3-yl, 4-methyl-2-oxooxan-4-yl, 2-oxo-1,3-dioxolan-4-ylmethyl, or 5-methyl-2-oxooxolan-5-yl.
 19. A polymer according to claim 12, wherein at least one of R¹⁰ to R¹³ is 2-oxooxolan-3-yloxycarbonyl, 4,4-dimethyl-2-oxooxolan-3-yloxycarbonyl, 4-methyl-2-oxooxan-4-yloxycarbonyl, 2-oxo-1,3-dioxolan-4-ylmethyloxycarbonyl, and 5-methyl-2-oxooxolan-5-yloxycarbonyl, and the remainder of R¹⁰ to R¹³ are each independently H, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl and butyladamantyl.
 20. A polymer according to claim 12, wherein at least one of R¹⁰ to R¹³ is 1-oxo-2-oxapropane-1,3-diyl, 1,3-dioxo-2-oxapropane-1,3-diyl, 1-oxo-2-oxabutane-1,4-diyl, or 1,3-dioxo-2-oxabutane-1,4-diyl, and the remainder of R¹⁰ to R¹³ are each independently a divalent group corresponding to a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms with one hydrogen atom eliminated, wherein said alkyl group is selected from methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl and butyladamantyl.
 21. A polymer according to claim 12, wherein R¹⁴ is norbornyl, bicyclo[3.3.1]-nonyl, tricyclo[5.2.1.0^(2,6)]decyl, adamantyl, ethyladamantyl, butyladamantyl, norbornylmethyl, or adamantylmethyl.
 22. A polymer according to claim 12, wherein R¹⁵ is a tertiary alkyl group of 4 to 20 carbon atoms, a trialkylsilyl group in which each alkyl moiety has 1 to 6 carbon atoms, an oxoalkyl group of 4 to 20 carbon atoms, tetrahydrofuran-2-yl, 2-methyltetrahydrofuran-2-yl, tetrahydropyran-2-yl, 2-methyltetrahydropyran-2-yl, tert-butoxycarbonyl, tert-butoxycarbonylmethyl, tert-amyloxycarbonyl, tert-amyloxycarbonylmethyl, 1,1-diethylpropyloxycarbonyl, 1,1-diethylpropyloxycarbonylmethyl, 1-ethylcyclopentyloxycarbonyl, 1-ethylcyclopentyloxycarbonylmethyl, 1-ethyl-2-cyclopentenyloxycarbonyl, 1-ethyl-2-cyclopentenyloxycarbonylmethyl, 1-ethoxyethoxycarbonylmethyl, 2-tetrahydropyranyloxycarbonylmethyl, 2-tetrahydrofuranyloxycarbonylmethyl, 1-methylcyclopentyl, 1-ethylcyclopentyl, 1-n-propylcyclopentyl, 1-isopropylcyclopentyl, 1-n-butylcyclopentyl, 1-sec-butylcyclopentyl, 1-methylcyclohexyl, 1-ethylcyclohexyl, 3-methyl-1-cyclopenten-3-yl, 3-ethyl-1-cyclopenten-3-yl, 3-methyl-1-cyclohexen-3-yl, 3-ethyl-1-cyclohexen-3-yl group, or is a group selected from the following formula:


23. A polymer according to claim 12, wherein, in addition to (i) the monomer of formula (1) and (ii) the monomer or monomers of formulas (2) to (10), the polymer has copolymerized therewith (iii) another monomer having a carbon-to-carbon double bond other than (i) and (ii).
 24. A polymer according to claim 23, wherein additional monomer (iii) is methyl methacrylate, methyl crotonate, dimethyl maleate, and dimethyl itaconate, unsaturated carboxylic acids such as maleic acid, fumaric acid, itaconic acid, norbornene, methyl norbornene-5-carboxylate, or itaconic anhydride.
 25. A polymer according to claim 12, wherein said polymer contains 20 to 90 mol % of units of formula (1a-1), formula (1a-2), or combinations thereof; 1 to 95 mol % of units of one or more types of formulae (2a) to (10a), and 0 to 80 mol % of one or more types derived from additional monomers (iii) having a carbon-to-carbon double bond other than (i) and (ii). 